Physical, chemical and pozzolanic properties of bricks of X-X zone of Karacahisar castle, Turkey
Üst veriTüm öğe kaydını göster
The objective of this study was to analyze the similar and different properties of historic bricks used in X-X zone of old Byzantium Castle Karacahisar Castle and according this knowledge to provide a reference for the bricks which will be used for the restoration here in the future. In order to perform this research, physical, pozzolanic and chemical analyses were carried out to structural adobe bricks. According to the analysis, it was found that water absorption percentage by weight under atmospheric pressure is between 11,825,3%, apparent porosity and water absorption by volume percent is between 22,238,2%. Apparent density of bricks is between 1,51-1,89 gr/cm(3) and real density is between 2,37-2,61 gr/cm(3). According to the ignition loss analysis, the CaCO3 content percent is between 1-19,4 % and the bricks do not have good pozzolanic properties.
KaynakConstruction Materials and Structures
- Bildiri Koleksiyonu 
- WoS İndeksli Yayınlar Koleksiyonu 
Başlık, yazar, küratör ve konuya göre gösterilen ilgili öğeler.
Assessment of Natural Radioactivity in Concrete Block, Extruded Clay Brick, and Mud Brick Taken From Ogbomoso, Southwestern, Nigeria Ayinmode, Bolaji Omogbemiga; Famakinwa, Rebecca Oluwadamilola; Ajayı, Jonathan Olanipekun (Anadolu Üniversitesi, 2012)This study evaluates the natural radioactivity in concrete block, extruded clay brick, and mud brick taken from Ogbomoso city. The six samples were collected from different part of the city, and were analyzed using highly ...
An experimental investigation on fly ash based geopolymer bricks Geopolymer bricks were produced by using F type fly ash, C type fly ash, sodium hydroxide solution, sodium silicate solution by means of pressure forming process. Then, the geobricks were heat treated at the temperature ...
The use of fired roof tile and brick wastes in stoneware bodies as alternative raw materials In this study, the utilization capability of the solid wastes taken from a commercial roof tile and brick factory in Eskisehir of Turkiye has been investigated in the production of stoneware bodies which can be formed by ...