Mg+2 and Ce+3 doped alpha-SiAlON ceramics

Abstract

In the present work, stabilization of MgO and CeO2 in alpha-SiAlON structure is studied. Mg and CeO2 were used in 50:50 molar ratios as additives. The mixture was sintered at 1830degreesC for 1 hour in gas pressure sintering furnace (GPS). The results show that sintered sample was composed of alpha-SiAlON and beta-SiAlON phases. According to X-ray diffraction (XRD) and energy dispersive X-ray measurements (EDX) analyses, Mg and Ce cation could be incorporated into alpha-SiAlON structure higher than single R cation (R=Mg or Ce) doped compositions.