Production and industrial adaptation of fast single firing wall tile opaque glass-ceramic glazes containing borax solid wastes

Abstract

Zircon (zirconium silicate) is the main opacifier of glossy, opaque, white colored, frit-based wall tile glazes. However, zirconia containing frits employed in the preparation of these glazes increase the production cost and therefore, limit zircon usage as a raw material at industrial scale. With the present study, it was searched whether borax solid wastes could be evaluated as a component in the starting relevant frit recipes. The wastes were obtained from Eti Maden Kirka Boron Company of Turkiye. Frit production, glaze preparation, application, and fast single-firing of glazed wall tiles were conducted under laboratory working conditions in Anadolu University, Department of Materials Science and Engineering laboratories. Beside standard tests applied to the final glazed wall tiles, color and gloss analyses of the fired glazes were conducted with a spectrophoto-meter and a gloss-meter. Characterization of these newly produced glass-ceramic glazes was made by X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) techniques.