Transmission electron microscopy studies of La2O3-doped alpha-SiAlON ceramics
(IOP Publishing LTD, 1999)
alpha-SiAlON is able to accommodate cations into its crystal structure if the cations are sufficiently small in size, thus helping to reduce the volume of the remnant grain boundary phase after processing. In this study, ...
Preparation of multiple-cation alpha-SiAlON ceramics containing lanthanum
(Amer Ceramic Soc, 1999)
Until recently, it was accepted that Ce3+ cations, with an ionic radius (r) of 1.03 Angstrom, were too large to form an alpha-SiAlON structure. However, more-recent studies have shown that cerium cations can be incorporated ...
Preparation of multiple-cation ?-SiAlON ceramics containing lanthanum
(1999)
Until recently, it was accepted that Ce 3+ cations, with an ionic radius (r) of 1.03 Å, were too large to form an ?-SiAlON structure. However, more-recent studies have shown that cerium cations can be incorporated into ...
?ݧ Sialon Transformation in Calcium-containing ? -SiAlON Ceramics
(1999)
Recent studies on rare earth densified ?-sialon ceramics have shown that the resulting ?-sialon product, present either as a single phase or in conjunction with ß-sialon, is unstable when heat treated at lower (1350-1600°C) ...
New developments in ? -SiAlON ceramics
(1999)
Two different ?-sialon compositions have been densified by either pressureless sintering or capsul-free sinter HIPing using either single cation namely strontium, lanthanum, cerium, neodymium or their equimolar mixtures ...