Thermal shock behaviour of alumina-mullite-zircon refractories
(Trans Tech Publications LTD, 2004)
Thermal shock behaviour of alumina-mullite-zircon refractories was investigated by varying zircon content. Thermal shock parameters R and R-st based on the room temperature mechanical measurements were calculated as a ...
The influence of fine alumina particles on the mechanical properties and thermal shock behaviour of slip-cast alumina-mullite refractories
(Trans Tech Publications LTD, 2004)
The object of this work is to improve understanding of relationships between microstructure and those mechanical properties likely to affect thermal shock behaviour of slip-cast alumina-mullite refractories. The incorporation ...
Spinel formation, reaction conditions and densification properties of magnesia-spinel composites
(Trans Tech Publications LTD, 2004)
Densification, reaction conditions and properties of densified MgO and spinel composites were examined using both pressureless sintering and hot-pressing. Initially fine (32 nm) MgO powder, either alone or blended with mum ...
Mechanical properties and thermal shock behaviour of model MgO-MgAl 2O4 spinel composite refractories
(2006)
The effects of varying the amounts (5 to 30 wt%) and particle sizes of magnesium aluminate spinel (i.e. preformed and in-situ formed) incorporated in a fully dense MgO, were investigated. Mechanical properties were measured ...
Mechanical properties of alumina-mullite-zircon refractories
(Trans Tech Publications LTD, 2004)
The relationships between mechanical properties and microstructure of alumina-mullite-zircon refractories were investigated by varying zircon content. Various sintering temperatures were used for the slip-cast refractories ...
The corrosion resistance of alumina-mullite-zircon refractories in molten glass
(Trans Tech Publications LTD, 2004)
Corrosion measurements on a set of alumina-mullite-zircon refractories have been carried out using a static crucible test consisting of a "hole in a block". Rates of corrosion of the refractory at 1370 degreesC for 72 h ...
Investigation of parameters affecting formation of mullite from kaolin
(Trans Tech Publications LTD, 2004)
This study aims to improve the understanding of formation of mullite from kaolin at low process temperature using different sintering regimes. The optimum parameters affecting mullite formation from kaolin such as sintering ...