Sintering behaviour of precursor mullite powders and resultant microstructures
(Elsevier BV, 1996)
Crystallization and sintering behaviour of two structurally different diphasic precursor mullite powders were studied. Powder derived from boehmite and colloidal silica formed mullite at around 1250°C and could be sintered ...
? › ß reverse phase transformation in silicon carbide in silicon nitride-particulate-reinforced-silicon carbide composites
(American Ceramic Society, 1996)
The ? › ß reverse transformation in SiC is observed in Si3N4-particulate-reinforced-SiC composites made from as-received ?-SiC and ?-Si3N4 powders. However, the transformation does not occur to any great extent in composites ...