Corrosion inhibition benzotriazole and N-mesyl benzotriazole on low carbon steel in sulfuric acid

Abstract

This study examines usage of benzotriazole (Bt) and N-mesyl benzotriazole (BtSO2CH3) for improvement of corrosion resistance of low carbon steel (LCS) in 0.1 M sulfuric acid (H2SO4). The inhibitor effect of Bt and BtSO2CH3 on the corrosion behavior of LCS was studied using electrochemical impedance spectroscopy (EIS), potentiodynamic polarization curves and polarization resistance techniques. Under investigated experimental conditions these compounds showed a good corrosion inhibition. The inhibition efficiency of BtSO2CH3 was more than that of Bt. The potentiodynamic polarization curves indicated that compounds are mixed type inhibitors. The inhibiting properties of compounds were found to depend on the concentration. The adsorption mechanism of compounds was investigated using different adsorption isotherms. The equilibrium constants and free energies of adsorption using the adsorption isotherms were calculated.

Bu çalışma 0,1 M sülfürik asit içinde düşük karbon çeliğinin (LCS) korozyon direncini arttırmak için benzotriazol (Bt) ve yeni sentezlenen N-mesil benzotriazol (BtSO2CH3) kullanımını incelemektedir. LCS’nin korozyon davranışına karşı Bt ve BtSO2CH3’ün inhibitör etkisi, elektrokimyasal empedans spektroskopisi (EIS), potansiyodinamik polarizasyon eğrileri ve polarizasyon direnci teknikleri kullanılarak çalışılmıştır. Belirtilen deneysel koşullarda bu bileşikler iyi bir korozyon inhibisyonu göstermektedir. BtSO2CH3’ün inhibitör etkinliği, Bt’ün inhibitör etkinliğinden daha fazladır. Potansiyodinamik polarizasyon eğrileri bileşiklerin karma inhibitör olduğunu göstermektedir. Bileşiklerin inhibisyon özelliklerinin derişime bağlı olduğu bulunmuştur. Bileşiklerin adsorpsiyon mekanizmaları farklı adsorpsiyon izotermleri kullanılarak incelenmiştir. Aynı zamanda serbest enerji ve denge sabiti değerleri adsorpsiyon izotermlerinden hesaplanmıştır.