Effects of cobalt, copper, manganese and titanium oxide additions on the microstructures of zinc containing soft porcelain glazes
(2002)
Different types of glazes, which are nearly all based upon silicate compositions, are used to meet a wide range of requirements in service. Many artistic effects are achieved by departing from a clear, smooth, transparent ...
Chemical durability behaviour of bulk glasses in the SrO-Mn2O3Fe2O3-MgO-ZrO 2-SiO2 (SMFMZS) system
(2001)
It is known that the SrO-MgO-ZrO2-SiO2 (SMZS) system glasses with 40 weight % silica content seem to give a very high chemical endurance against highly alkaline solutions and can be recommended for the reinforcement of ...
The development and characterisation of zinc crystal glazes used for Amakusa-like soft porcelains
(Elsevier Sci LTD, 2000)
In porcelain production, as well as bodies expected to have white colour, compaction and translucency, suitable glaze compositions have great importance from both a technological and decoration point of view. Supplying the ...
The effect of albite wastes on glaze properties and microstructure of soft porcelain zinc crystal glazes
(Elsevier Sci LTD, 2001)
The efficient utilisation of waste materials arising from diverse industrial branches is of technological importance. As a replacement material for feldspar in some soft porcelain zinc crystal glazes, albite triage wastes ...
Effect of cobalt oxide and copper oxide additions to zinc-containing soft porcelain glazes
(Amer Ceramic Soc, 2001)
…
Crystallisation in the SrO-MgO-ZrO2-SiO2 (SMZS) system glasses
(Kluwer Academic Publ, 2002)
The SrO-MgO-ZrO2-SiO2 quaternary system was first investigated in 1989. It was reported that the lowest liquidus temperature is as similar to1000degreesC and located near the SrO-SiO2 edge of the composition tetrahedron. ...
Compositional modifications to floor tile glazes opacified with zircon
(I O M Communications LTD Inst Materials, 2001)
In the ceramic tile industry opaque glazes with considerable zircon content are widely used. However, the high cost of zircon limits its wide use in relevant glaze compositions. In the present study, a model opaque glaze ...
Melting behaviour of glasses in the SrO-MgO-ZrO2-SiO2 system
(Soc Glass Technology, 1999)
In the SrO-MgO-ZrO2-SiO2 system a large range of compositions with 60, 55, 50, 45, 40 and 35 wt% silica has been thoroughly investigated The effect of silica and other constituents on melting, annealing and colour variations ...