Phase studies of reactive infiltrated boron carbide-aluminium composites by quantitative XRD
(Trans Tech Publications LTD, 2002)
Fully dense (> 98 % of theoretical) boron carbide (B4C)-aluminium (Al) composites were produced between 985 degrees and 1370 degreesC by pressureless melt infiltration of Al alloys into porous B4C compacts under an argon ...
Mechanical properties of melt infiltrated boron carbide-aluminium composites
(Trans Tech Publications LTD, 2002)
Boron carbide (B4C)-aluminium (Al) composites were produced by melt infiltration of 2024-T3 series Al alloys into porous B4C compacts in the temperature range of 985 degrees -1370 degreesC under an inert atmosphere (Ar). ...
Transmission electron microscopy of SrO containing multi-cation doped alpha-SiAlON ceramics
(Trans Tech Publications LTD, 2002)
An advantage of alpha-SiAlON is that it can accommodate cations of sintering additives and hence reduces the amount of deleterious remnant intergranular amorphous phase. However, it is believed that relatively large cations ...
Transmission electron microscopy of SrO containing multi-cation doped ?-SiAlON ceramics
(2002)
An advantage of ?-SiAlON is that it can accommodate cations of sintering additives and hence reduces the amount of deleterious remnant intergranular amorphous phase. However, it is believed that relatively large cations ...
Seramik sanayii hızlı pişirim fırınlarda kullanılan rulo malzemesi müllitin üretimi ve mekanik özelliklerinin belirlenmesi
(1999)
Bu çalışmada, $\alpha-Al_2O_3$ ve kaolin kullanılarak, müllit $(3Al_2O_3. 2SİO_2)$ matriks elde edilmiş ve bu malzemenin seramik hızlı pişirim fırınlarının bir yapı elemanı olan döner rulo malzemesi yerine kullanılabilme ...
Hydrated aluminium sulfate precipitation by enzyme-catalysed urea decomposition
(Elsevier Sci LTD, 2000)
Hydrated basic aluminium hydroxide precipitates were obtained from aluminium sulphate solution at room temperature and at 92 degrees C by using urea. Enzyme urease was used to decompose urea at room temperature. It was ...
Microstructural characterisation of melt infiltrated boron carbide-aluminium composites
(IOP Publishing LTD, 2001)
The microstructure of boron carbide (B4C) - aluminium (Al) composites produced by reactive infiltration were characterised using a scanning electron microscope (SEM) and a transmission electron microscope (TEM) both attached ...
Microstructural characterization of reactively sintered mullites
(Amer Ceramic Soc, 2000)
Mullite ceramics have been produced by reaction sintering of powders prepared using pseudoboehmite-colloidal silica and aluminum sulfate-colloidal silica mixtures. The microstructural development of these mullites was ...
Microstructural characterization of surface layers formed on a low alloy steel during erosion - oxidation in a fluidized bed
(Chapman Hall LTD, 1997)
Low alloy steel specimens were subjected to erosion-oxidation in a simulated fluidized bed environ ment in the range 100-600 degrees C. Transmission electron microscopy was carried out on the surfaces which experienced ...
Transmission electron microscopy studies of La2O3-doped alpha-SiAlON ceramics
(IOP Publishing LTD, 1999)
alpha-SiAlON is able to accommodate cations into its crystal structure if the cations are sufficiently small in size, thus helping to reduce the volume of the remnant grain boundary phase after processing. In this study, ...